initial permeability
英 [ɪˈnɪʃl ˌpɜːmjəˈbɪlɪti]
美 [ɪˈnɪʃl pərmiəˈbɪlɪti]
起始磁化率
双语例句
- The analysis has been conducted to the impact of different initial permeability on gas drainage, and the result is that the larger the initial, permeability, the more easily gas drainage is.
分析了不同的初始渗透率对抽放瓦斯的影响，初始渗透率越大，瓦斯越易抽放。 - When 10 mol% CuO is added, the finest microstructure of the ferrite and the most homogeneous particles are obtained; and hence the ferrite achieved the best initial permeability, the lowest compare spoilage coefficient and compare temperature coefficient.
当CuO含量为10mol%时，铁氧体的显微结构最为致密，晶粒尺寸分布也最为均匀，并且能够获得最高的初始磁导率和最低的比损耗系数、比温度系数。 - The result indicated that better microstructure, higher initial permeability, lower loss and higher density can be obtained for higher quenching speed.
发现随着冷却速度的加快，可获得更好微观结构、更高起始磁导率、更低损耗、更高烧结密度之低温共烧材料。 - The research of the high initial permeability ( 6000~ 20000) ferrite and the frequency dependence of inductance of the ferrite transformer made by high permeability ferrite core are presented.
研究了高起始磁导率（6000～20000）铁氧体和由该磁芯制成的变压器的电感频率依赖关系。 - After annealing in a rotating field, the initial permeability of films is not less than 3000, at the field up to 10 MHz, and they show a good frequency response!
经旋转磁场退火热处理后，膜的起始磁导率一直到10MHz都可在3000以上，表现出良好的频率特性。 - And sintering temperature has an important effect on the initial permeability of Mn-Zn ferrites.
烧结温度对锰锌铁氧体的起始磁导率有重要影响。 - A new method of defining stress sensitivity coefficient was presented. The relationship between stress sensitivity coefficient and initial permeability was deduced by physical modeling experiment in room.
提出了一种定义应力敏感系数的新方法，通过室内物理模拟实验，分析得到了应力敏感系数与初始渗透率的关系式。 - However, permeability has also recovered to a certain degree with the waterflooding to be prolonged, and the degree of recovery is related to the extent of initial permeability: the degree of recovery is greater with higher initial permeability;
但随注水时间的延长，渗透率有不同程度的恢复，且恢复程度与渗透率大小有关：初始渗透率高，恢复程度大； - Weak magnetic field the induced current of the steel specimens is proportional to initial permeability.
并证实了在断开磁路下的交流弱磁场中，感应电流与钢铁试样的μ0成正比。 - When excessive MoO-3 added, porosity and core losses increased, the initial permeability decreased.
但掺杂过量时，晶粒中气孔率增加，起始磁导率下降，损耗也大为增加。